Borosilicate glass of high chemical resistance and low viscosity which contains zirconium oxide and lithium oxide

ABSTRACT

The invention relates to a borosilicate glass of high chemical resistance and low viscosity which contains zirconium oxide and lithium oxide. The borosilicate glass has hydrolytic resistance (in accordance with DIN ISO 719), class 1 acid resistance (in accordance with DIN 12116), and class 1 alkali resistance (in accordance with DIN ISO 659), and with a low operating temperature V A  of between 1180° C. to 1230° C. and a coefficient of thermal expansion α 20/300  of 4.9×10 -6  K -1 . The borosilicate glass has the composition (in % by weight, based on oxide): SiO 2  73-75; B 2  0 3  7-10; Al 2  0 3  5-7; ZrO 2  1-3; Li 2  0 0.5-1.5; Na 2  0 0-10; K 2  0 0-10; MgO 0-3; CaO 0-3; BaO 0-3; SrO 0-3; ZnO 0-3; ratio of SiO 2  /B 2  0 3  ≧7.5; Σ SiO 2  +Al 2  0 3  +ZrO 2  80-83 and Σ MgO+CaO+BaO+SrO+ZnO≦3, and fluorides 0-3. The glass is particularly suitable for use as a versatile primary packaging material for pharmaceuticals, for example as ampule glass.

FIELD OF THE INVENTION

The invention relates to a borosilicate glass which contains zirconium oxide and lithium oxide and has class 1 hydrolyric resistance, acid resistance and alkali resistance. The borosilicate glass of the invention has a low viscosity, in particular in the processing range.

BACKGROUND OF THE INVENTION

For use as primary packaging material, for example, as ampule glass, the pharmaceutical industry requires glasses having extremely high chemical resistance. The commercial pharmaceutical ampule glasses known up to now are in hydrolytic resistance class (H) 1 (in accordance with DIN ISO 719), acid resistance class (S) 1 (in accordance with DIN 12116) and alkali resistance class (L) 2 (in accordance with DIN ISO 695). This prior art is represented by the glass FIOLAX® clear, Code No. 8412 (SiO₂ 74.7; B₂ O₃ 10.0; Al₂ O₃ 5.0; Na₂ O 6.5; CaO 1.5; BaO 2.0; fluorides 0.3% by weight) and JENA^(er) instrument glass Ggl 490/5 (SiO₂ 73.2; B₂ O₃ 11.0; Al₂ O₃ 5.3; Na₂ O 7.0; K₂ O 0.2; CaO 0.8; BaO 2.5% by weight), which have a weight loss of 100 mg/dm² (in accordance with DIN ISO 695). A class 1 alkali resistance, that is, a weight loss of <75 mg/dm², has so far not been achieved by commercial pharmaceutical ampule glasses.

However, an important requirement in the pharmaceutical industry is the provision of primary packaging materials having significantly improved alkali resistance to enable packaging of recently developed injection substances which exert a stronger alkaline attack on the container. Practical experience has shown that the development of glasses in the laboratory having weight losses of less than 65 to 70 mg/dm², that is, safely within alkali class 1, is required in order to maintain alkali resistance in the production process.

However, the achievement of this requirement must not impair the other important glass characteristics and glass production properties. For example, H=1 and S=1 must be maintained. Furthermore, the coefficient of linear thermal expansion α_(20/300) should be about 4.9=10⁻⁶ K⁻¹, corresponding to that of the commercial glasses FIOLAX®clear, Code No. 8412 and Ggl 490/5. Also, for quality and cost reasons, the viscosity must not be too high over the entire melting, processing and cooling range.

An essential parameter for characterizing the processability of the glass is the processing temperature (V_(A)) at which the viscosity of the glass is 10⁴ dPas. For pharmaceutical ampule glass, this V_(A) value should not be more than 1220° C. to 1230° C. in order to prevent the occurrence of disadvantageous evaporation phenomena of glass components, principally alkali metal oxides and boric acid, and to save energy costs during production of tubes and during subsequent conversion of the tubes into ampules. Evaporation occurring during thermoforming of the glass can make the ampules unusable.

The glass viscosity in the cooling region is characterized by the glass transformation temperature T_(g), which corresponds to a viscosity of approximately 10¹³ dPas. This temperature should likewise not be too high, in order to save energy costs in the cooling region.

Pharmaceutical container glasses, as described in German patent publications 3,722,130 and DD 301,821, do not satisfy these high requirements.

Glasses having a composition as indicated in German patent publication 3,722,130 do not fall within alkali class 1. U.S. Pat. No. 5,459,110 discloses a lamp glass and fire protective glass having a specific composition and having an alkali resistance in class 1. Although L=1 is achieved by some glasses having a composition as described in DD 301,821, it is evident that, on the one hand, alkali resistance class 1 is only just achieved, if at all, and, on the other hand, the weight loss in the alkali resistance test shows scattered values when the melt having a certain composition is repeated a number of times, so that L=1 is not always achieved. Improvements are thus necessary here to obtain an alkali resistance reserve.

SUMMARY OF THE INVENTION

It is the object of the invention to provide borosilicate glasses of high chemical resistance and low viscosity, principally having class 1 hydrolyric resistance (in accordance with DIN ISO 719), class 1 acid resistance (in accordance with DIN 12116) and in particular, class 1 alkali resistance (in accordance with DIN ISO 659) with a weight loss of from <65 to 70 mg/dm², operating temperatures of <1220° C. to 1230° C. and a coefficient of linear thermal expansion of α_(20/300) =4.8 to 5.0×10⁻⁶ K⁻¹.

DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION

The borosilicate glass composition of the invention is of high chemical resistance and low viscosity and contains zirconium oxide and lithium oxide. The glass composition includes in percent by weight on oxide basis: SiO₂ 73.0-75.0; B₂ O₃ 7.0-10.0; Al₂ O₃ 5.0-7.0; ZrO₂ 1.0-3.0; Li₂ O 0.5-1.5; Na₂ O 0-10.0; K₂ O 0-10.0; MgO 0-3.0; CaO 0-3.0; BaO 0-3.0; SrO 0-3.0; ZnO 0-3.0; fluorides 0-3.0; with SiO₂ /B₂ O₃ ≧7.5; Σ SiO₂ +Al₂ O₃ +ZrO₂ 80.0-83.0; Σ MgO+CaO+BaO+SrO+ZnO ≦3.0.

Glasses having H=1, S=1, L=1 (weight loss <65 to 70 mg/dm²), V_(A) values of <1230° C. and α_(20/300) values of 4.8 to 5.0×10⁻⁶ K⁻¹ can be produced in the range of compositions (% by weight, based on oxide), SiO₂ 73.0-75.0 (preferably 73.5-75.0); B₂ O₃ 7.0-10.0 (preferably 8.0-10.0); Al₂ O₃ 5.0-7.0 (preferably 5.0-6.0); ZrO₂ 1.0-3.0 (preferably 1.0-2.5); Li₂ O 0.5-1.5; Na₂ O 0-10.0; K₂ O 0-10.0; MgO 0-3.0; CaO 0-3.0; BaO 0-3.0; SrO 0-3.0; ZnO 0-3.0 and fluorides 0-3.0 if the ratio of the glass formers SiO₂ to B₂ O₃ is ≧7.5; the sum SiO₂ +Al₂ O₃ +ZrO₂ is 80.0-83.0 percent by weight and the sum of the divalent additives MgO+CaO+BaO+SrO+ZnO is ≧3.0 percent by weight. The sum of the alkali metal oxides Li₂ O+Na₂ O+K₂ O is preferably limited to 7.0-10.0 percent by weight.

The following composition range (% by weight, based on oxide) is particularly preferred: SiO₂ 73.5-75.0; B₂ O₃ 8.0-10.0; Al₂ O₃ 5.0-6.0; ZrO₂ 1.0-2.5; Li₂ O 0.5-1.5; Na₂ O 0.5-5.0; K₂ O 0.5-5.0; CaO 0.5-2.0, with SiO₂ /B₂ O₃ ≧7.5; Σ SiO₂ +Al₂ O₃ +ZrO₂ 81.0-83.0; and Σ Li₂ O+Na₂ O+K₂ O 7.0-9.5.

The glasses also have further advantageous properties which are essential for flaw-free and cost effective mass production. For example, they satisfy the requisite conditions placed on the melting behavior, the crystallization stability and demixing stability, the electrical conductivity, the corrosion behavior vis-a-vis refractory materials, the refining properties, the evaporation properties, et cetera.

Starting from the rounded composition of the common container glass type (in % by weight, based on oxide) SiO₂ 75; B₂ O₃ 11; Al₂ O₃ 5; Σ Na₂ O+K₂ O 7; Σ BaO+CaO 2, the optimizations which have resulted in the composition of the invention are as explained below.

In order to achieve class 1 alkali resistance with a weight loss of from <65 to 70 mg/dm² and at the same time a relatively low processing temperature of V_(A) <1220° C. to 1230° C., both ZrO₂ in an amount of from 1 to 3% by weight and Li₂ O (completely absent in German patent publication 3,722,130) in an amount of 0.5-1.5% by weight must be added to the borosilicate glass described above. In addition, the ratio between the glass formers SiO₂ and B₂ O₃ must be greater than or equal to 7.5. The composition of the invention differs from those of German patent publications 3,722,130 and DD 301,821 because of this ratio and because of the relatively low content of B₂ O₃ (7.0-10.0 percent by weight).

By varying other components (Al₂ O₃, alkali metal oxides, alkaline earth metal oxides or ZnO), the composition can be optimized, and the other important glass or glass production properties can be improved or matched.

The solution found is all the more surprising since the general borosilicate glass SiO₂ --B₂ O₃ --Al₂ O₃ --M₂ O--MO--AC (=additional components) has been known for some time, has been investigated scientifically on many occasions and is used in practice for a variety of applications.

Furthermore, optimization calculations based on linear models are unsuitable for determining this composition range with an advantageously high alkali resistance, since the alkali resistance of the glass does not increase in a linear manner with increasing SiO₂ /B₂ O₃ ratio. For this reason, a calculation of this type would not determine the range of low weight loss.

The addition of ZrO₂ and the small amount of B₂ O₃ improve the resistance to water, acids and alkali. However, the addition of ZrO₂ is limited by its low solubility in the glass and the increase in the viscosity of the glass. The required reduction in the B₂ O₃ content also causes an increase in viscosity, but this can be compensated by adding alkali metal oxides, in particular Li₂ O.

When selecting the alkali metal oxides, various aspects should be considered: excessive amounts of Li₂ O in the glass melt cause an unacceptably strong attack on the refractory material of the melting chamber so that 0.5-1.5% by weight of Li₂ O represents an optimum. Just as Li₂ O evaporates less than Na₂ O from the melt of the borosilicate glass under consideration, the vapor pressure of Na₂ O is less than that of K₂ O. This suggests (at the given maximum Li₂ O content) exclusive or predominant use of Na₂ O. The lower costs of the Na₂ O raw materials are a further argument.

In particular applications of the glass of the invention, for example, the production of photomultiplier tubes, it is even imperative to omit the use of K₂ O entirely. This is because the K₂ O raw materials can contain extremely small amounts of radioactive impurities, which would under certain circumstances cause an increase in the noise level in the photomultiplier.

By contrast, larger amounts of K₂ O must be used in low-CaO and CaO-free synthetic variants in order to produce the desired α_(2O/300) value.

For CaO-free syntheses, the following composition range (% by weight, based on oxide) is advantageous: SiO₂ 73.5-75.0; B₂ O₃ 8.0-10.0; Al₂ O₃ 5.0-6.0; ZrO₂ 1.0-2.5; Li₂ O 0.5-1.5; Na₂ O 0-3.0; K₂ O 4.0-7.0 with SiO₂ /B₂ O₃ ≧7.5; Σ SiO₂ +Al₂ O₃ +ZrO₂ 81.0-83.0; Σ Li₂ O+Na₂ O+K₂ O 7.0-10.0.

It is also known that a high Na₂ O content in the conversion of tubes into ampules by reheating the glass at high deformation temperatures can result particularly quickly in efflorescence on the glass surface. However, this can be countered simply by reducing the V_(A) value by addition of ZrO₂ and Li₂ O and also by the sole use of K₂ O or the simultaneous use of K₂ O and Na₂ O and by addition of small amounts of ZnO.

The evaporation products in industrial borosilicate glasses, usually metaborates, have at high temperatures, independently of the type of alkali metal oxide (M₂ O) used, a boric acid modulus of Ψ=B₂ O₃ /(B₂ O₃ +M₂ O) (in mol %) of from 0.53 to 0.58. This comes very close to the boric acid modulus of the glass composition, which makes evaporation easier. For this reason, it is necessary to reduce the evaporation during the melting process by other means, namely by a judicious increase in the viscosity.

This is achieved by means of relatively high contents of SiO₂ (73.0-75.0% by weight) and Al₂ O₃ (5.0-7.0% by weight).

An Al₂ O₃ content of this level represents a further distinction of the glass composition of the invention from the compositions of DD 301,821. The glass compositions of DE 4,230,607 also contain significantly less Al₂ O₃, at 1.5-4.0% by weight.

If the proportion of the SiO₂ and Al₂ O₃ is increased even further than according to the invention, the viscosity and thus also the V_(A) value increase too much, which also impairs refining. High Al₂ O₃ contents also result in a noticeable impairment of the acid resistance.

Taking into account all the advantageous and disadvantageous effects of the constituents of a high-quality, versatile pharmaceutical ampule glass of this type, the following glass composition (% by weight, based on oxide) has proven particularly advantageous: SiO₂ 74.0-74.5; B₂ O₃ 8.5-9.5 (particularly preferable 9.0-9.5); Al₂ O₃ 5.3-6.0 (particularly preferable 5.3-5.8); ZrO₂ 1.6-2.0; Li₂ O 0.7-1.3 (particularly preferable 0.9-1.1); Na₂ O 3.0-5.0; K₂ O 2.0-5.0 (particularly preferable 2.0-4.0); CaO 0.5-1.6 (particularly preferable 0.8-1.2); with Σ SiO₂ +Al₂ O₃ +ZrO₂ 81.3-82.0; and Σ Li₂ O+Na₂ O+K₂ O 7.0-9.5 (particularly preferable 7.0-9.0).

Thus, at an α value of approximately 4.9×10⁻⁶ K⁻¹, an excellent chemical resistance of H=1, S=1 and L=1 (weight loss <65 to 70 mg/dm²) and a V_(A) value of as low as ≦1200° C. is achieved.

Since CaO has a stabilizing action on the acid resistance, small amounts should be present in the glass if possible. Small amounts of BaO are likewise helpful in order to further reduce viscosity and to lower the melting point. On the other hand, it may also be necessary for the glass to contain only very little BaO and CaO, or none at all, since it is known that these components can react in an undesired manner with some specific injection solutions.

If the respective pharmaceutical and industrial areas of application do not make the highest demands regarding chemical resistance, the glass properties can be further modified by addition of the further bivalent components SrO, MgO and ZnO and by varying the CaO and BaO proportions.

However, the total content of these components must remain restricted to a maximum of 3.0% by weight, whereby the composition of the invention differs from the composition disclosed in German patent publication 4,230,607 (Σ MgO+CaO+BaO+ZnO+SrO+ZrO₂ =6 to 10 Σ MgO+CaO+BaO+ZnO+SrO =3 to 9.5 with ZrO₂ =0.5 to 3).

In addition, small amounts of fluorides can be added to the glass compositions of the invention in order to accelerate melting or to reduce the viscosity further. Also, known refining agents, such as chlorides and Sb₂ O₃, can be added.

Examples of the invention are presented below.

Table 1 shows glass compositions of the invention and their essential properties relating to the invention.

It can be seen that, if the pregiven coefficient of thermal expansion of α_(20/300) =4.9×10⁻⁶ K⁻¹ is maintained, the alkali resistance L, expressed by low weight loss values of from 58 to 65 mg/dm², is very safely within class 1, and the operating temperatures are low, with V_(A) values from 1180° C. to 1220° C.

                  TABLE 1                                                          ______________________________________                                         Examples of glasses of the invention                                           (glass compositions in percent by weight)                                      Glass Number 1       2       3     4     5                                     ______________________________________                                         SiO.sub.2    74.3    74.2    74.3  74.3  74.3                                  B.sub.2 O.sub.3                                                                             9.3     8.8     9.3   9.3   9.3                                   Al.sub.2 O.sub.3                                                                            5.5     5.8     5.5   5.5   5.5                                   ZrO.sub.2    1.8     1.8     1.8   1.8   1.8                                   Li.sub.2 O   1.0     1.0     1.0   1.0   1.0                                   Na.sub.2 O   4.0     3.0     3.5   3.0   2.0                                   K.sub.2 O    3.0     4.0     3.8   4.6   6.1                                   CaO          1.1     1.4     0.8   0.5   --                                    with                                                                           SiO.sub.2 /B.sub.2 O.sub.3                                                                  8.0     8.4     8.0   8.0   8.0                                   Σ SiO.sub.2 + Al.sub.2 O.sub.3 + ZrO.sub.2                                            81.6    81.8    81.6  81.6  81.6                                  Σ Li.sub.2 O + Na.sub.2 O + K.sub.2 O                                                 8.0     8.0     8.3   8.6   9.1                                   Essential glass                                                                properties                                                                     α.sub.20/300 (10.sup.-6 K.sup.-1)                                                     4.9     4.9     4.9   4.9   4.9                                   L (mg/dm.sup.2)                                                                             62      58      63    64    65                                    V.sub.A (°C.)                                                                        1180    1200    1190  1200  1220                                  ______________________________________                                    

The following data are given for Example 1 in order to demonstrate further advantageous properties:

Density ρ: 2.36 g/cm³

Transformation temperature T_(g) : 540° C.

Annealing temperature or point (A.P.): 550° C.

Softening point E_(w) : 785° C.

Crystallization and demixing stability: adequate for flaw-free production of the glass as a mass-produced product.

The T_(g) and A.P. temperatures confirm that the glass has a relatively low and thus favorable viscosity even in the cooling region so that inexpensive cooling is possible.

The glasses are produced in a conventional manner in a gas-heated laboratory furnace at 1620° C. in 0.5 liter crucibles over a period of about 4 hours, and are subsequently cast in metal molds to form blocks and are then cooled. The raw materials used were sand, H₃ BO₃, Al(OH)₃, alkali and alkaline earth metal carbonates and nitrates, zirconium dioxide and ZnO. The glasses exhibited good melting behavior. The raw materials used can also be those usually used for industrial glasses.

The glass of the invention is principally suitable for use as a versatile primary packaging material for pharmaceuticals, for example, as ampule glass. It can also be used as instrument glass for laboratory and other technical applications.

It is understood that the foregoing description is that of the preferred embodiments of the invention and that various changes and modifications may be made thereto without departing from the spirit and scope of the invention as defined in the appended claims. 

What is claimed is:
 1. A borosilicate glass composition of high chemical resistance and low viscosity which contains zirconium oxide and lithium oxide, said glass composition comprising in percent by weight on oxide basis:

    ______________________________________                                         SiO.sub.2            73.0-75.0                                                 B.sub.2 O.sub.3      7.0-10.0                                                  Al.sub.2 O.sub.3     5.0-7.0                                                   ZrO.sub.2            1.0-3.0                                                   Li.sub.2 O           0.5-1.5                                                   Na.sub.2 O            0-10.0                                                   K.sub.2 O             0-10.0                                                   MgO                  0-3.0                                                     CaO                  0-3.0                                                     BaO                  0-3.0                                                     SrO                  0-3.0                                                     ZnO                  0-3.0                                                     fluorides            0-3.0                                                     with                                                                           SiO.sub.2 /B.sub.2 O.sub.3                                                                          ≧7.5                                               Σ SiO.sub.2 + Al.sub.2 O.sub.3 + ZrO.sub.2                                                    80.0-83.0                                                 Σ MgO + CaO + BaO + SrO + ZnO                                                                 ≦3.0.                                              ______________________________________                                    


2. The borosilicate glass composition of claim 1, comprising in percent by weight on oxide basis:

    ______________________________________                                         SiO.sub.2            73.5-75.0                                                 B.sub.2 O.sub.3      8.0-10.0                                                  Al.sub.2 O.sub.3     5.0-6.0                                                   ZrO.sub.2            1.0-2.5                                                   Li.sub.2 O           0.5-1.5                                                   Na.sub.2 O            0-10.0                                                   K.sub.2 O             0-10.0                                                   MgO                  0-3.0                                                     CaO                  0-3.0                                                     BaO                  0-3.0                                                     SrO                  0-3.0                                                     ZnO                  0-3.0                                                     with                                                                           SiO.sub.2 /B.sub.2 O.sub.3                                                                          ≧7.5                                               Σ SiO.sub.2 + Al.sub.2 O.sub.3 + ZrO.sub.2                                                    80.0-83.0                                                 Σ Li.sub.2 O + Na.sub.2 O + K.sub.2 O                                                         7.0-10.0                                                  Σ MgO + CaO + BaO + SrO + ZnO                                                                 ≦3.0.                                              ______________________________________                                    


3. The borosilicate glass composition of claim 2, comprising in percent by weight on oxide basis:

    ______________________________________                                         SiO.sub.2         73.5-75.0                                                    B.sub.2 O.sub.3    8.0-10.0                                                    Al.sub.2 O.sub.3  5.0-6.0                                                      ZrO.sub.2         1.0-2.5                                                      Li.sub.2 O        0.5-1.5                                                      Na.sub.2 O        0.5-5.0                                                      K.sub.2 O         0.5-5.0                                                      CaO               0.5-2.0                                                      with                                                                           SiO.sub.2 /B.sub.2 O.sub.3                                                                       ≧7.5                                                  Σ SiO.sub.2 + Al.sub.2 O.sub.3 + ZrO.sub.2                                                 81.0-83.0                                                    Σ Li.sub.2 O + Na.sub.2 O + K.sub.2 O                                                       7.0-9.5.                                                    ______________________________________                                    


4. The borosilicate glass composition of claim 2, comprising in percent by weight on oxide basis:

    ______________________________________                                         SiO.sub.2         73.5-75.0                                                    B.sub.2 O.sub.3    8.0-10.0                                                    Al.sub.2 O.sub.3  5.0-6.0                                                      ZrO.sub.2         1.0-2.5                                                      Li.sub.2 O        0.5-1.5                                                      Na.sub.2 O          0-3.0                                                      K.sub.2 O         4.0-7.0                                                      with                                                                           SiO.sub.2 /B.sub.2 O.sub.3                                                                       ≧7.5                                                  Σ SiO.sub.2 + Al.sub.2 O.sub.3 + ZrO.sub.2                                                 81.0-83.0                                                    Σ Li.sub.2 O + Na.sub.2 O + K.sub.2 O                                                        7.0-10.0.                                                  ______________________________________                                    


5. The borosilicate glass composition of claim 3, comprising in percent by weight on oxide basis:

    ______________________________________                                         SiO.sub.2         74.0-74.5                                                    B.sub.2 O.sub.3   8.5-9.5                                                      Al.sub.2 O.sub.3  5.3-6.0                                                      ZrO.sub.2         1.6-2.0                                                      Li.sub.2 O        0.7-1.3                                                      Na.sub.2 O        3.0-5.0                                                      K.sub.2 O         2.0-5.0                                                      CaO               0.5-1.6                                                      with                                                                           Σ SiO.sub.2 + Al.sub.2 O.sub.3 + ZrO.sub.2                                                 81.3-82.0                                                    Σ Li.sub.2 O + Na.sub.2 O + K.sub.2 O                                                       7.0-9.5.                                                    ______________________________________                                    


6. The borosilicate glass composition of claim 5, comprising in percent by weight on oxide basis:

    ______________________________________                                         SiO.sub.2         74.0-74.5                                                    B.sub.2 O.sub.3   9.0-9.5                                                      Al.sub.2 O.sub.3  5.3-5.8                                                      ZrO.sub.2         1.6-2.0                                                      Li.sub.2 O        0.9-1.1                                                      Na.sub.2 O        3.0-5.0                                                      K.sub.2 O         2.0-4.0                                                      CaO               0.8-1.2                                                      with                                                                           Σ SiO.sub.2 + Al.sub.2 O.sub.3 + ZrO.sub.2                                                 81.3-82.0                                                    Σ Li.sub.2 O + Na.sub.2 O + K.sub.2 O                                                       7.0-9.0.                                                    ______________________________________                                     